AUTHOR=Wilks Seth J., Richardson-Burn Sarah M., Hendricks Jeffrey L., Martin David , Otto Kevin J.
TITLE=Poly(3,4-ethylene dioxythiophene) (PEDOT) as a micro-neural interface material for electrostimulation
JOURNAL=Frontiers in Neuroengineering
VOLUME=Volume 2 - 2009
YEAR=2009
URL=https://www.frontiersin.org/journals/neuroengineering/articles/10.3389/neuro.16.007.2009
DOI=10.3389/neuro.16.007.2009
ISSN=1662-6443
ABSTRACT=Chronic microstimulation-based devices are being investigated to treat conditions such as blindness, deafness, pain, paralysis and epilepsy. Small area electrodes are desired to achieve high selectivity. However, a major trade-off with electrode miniaturization is an increase in impedance and charge density requirements. Thus, the development of novel materials with lower interfacial impedance and enhanced charge storage capacity is essential for the development of micro-neural interface-based neuroprostheses. In this report, we study the use of conducting polymer poly(3,4-ethylene dioxythiophene) (PEDOT) as a neural interface material for microstimulation of small area iridium electrodes on silicon-substrate arrays. Characterized by electrochemical impedance spectroscopy, electrodeposition of PEDOT results in lower interfacial impedance at physiologically-relevant frequencies, with the 1kHz impedance magnitude being 23.3 ± 0.7 kΩ compared to 113.6 ± 3.5 kΩ for iridium oxide (IrOx) on 177μm2 sites. Further, PEDOT exhibits enhanced charge storage capacity at 75.6 ± 5.4 mC/cm2 compared to 28.8 ± 0.3 mC/cm2 for IrOx, characterized by cyclic voltammetry (50 mV/s). These improvements at the electrode interface were corroborated by observation of the voltage excursions that result from constant current pulsing. The PEDOT coatings provide both a lower amplitude voltage and a more ohmic representation of the applied current compared to IrOx. During repetitive pulsing, PEDOT-coated electrodes show stable performance and little change in electrical properties, even at relatively high current densities which cause IrOx instability. These findings support the potential of PEDOT coatings as a micro-neural interface material for electrostimulation.